Perpendicular exchange anisotropy in Mn-Ir/Fe-Co/[Pt/Co] 4 multilayers

Hirokazu Takahashi, Masakiyo Tsunoda, Migaku Takahashi

Research output: Contribution to journalArticlepeer-review

6 Citations (Scopus)

Abstract

The perpendicular unidirectional anisotropy constant, J K perp, of Mn-Ir/Fe-Co/[Pt/Co] 4 multilayers was investigated by systematically changing the Fe-Co layer composition, and was compared with the in-plane unidirectional anisotropy constant, J K in, of Mn-Ir/Fe-Co bilayers. Observed trends were similar for the variation of J K perp and J K in against the compositional change. This result indicates that the perpendicular exchange anisotropy and in-plane exchange anisotropy are induced by similar mechanisms. On the other hand, an apparent discrepancy was pointed out between the absolute values of J K perp and J K in in particular for the compositional region where Fe-Co forms body-centered-cubic (bcc) structure. This significant discrepancy in the bcc-Fe-Co region was explained by the magnetic anisotropy of the Fe-Co layer, and it is expected that J K perp could be increased as large as J K in when strong perpendicular magnetic anisotropy is induced in the Fe-Co layer.

Original languageEnglish
Article number6332948
Pages (from-to)4347-4350
Number of pages4
JournalIEEE Transactions on Magnetics
Volume48
Issue number11
DOIs
Publication statusPublished - 2012 Oct 29

Keywords

  • Compositional dependence
  • Exchange bias
  • Mn-Ir
  • Perpendicular exchange anisotropy
  • Perpendicular magnetic anisotropy

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Perpendicular exchange anisotropy in Mn-Ir/Fe-Co/[Pt/Co] <sub>4</sub> multilayers'. Together they form a unique fingerprint.

Cite this