Oxygen controlled melt growth process of filamentary Gd123 superconductors

Y. Adachi; T. Goto; K. Watanabe

doi:10.1016/S0921-4534(01)00551-2

Oxygen controlled melt growth process of filamentary Gd123 superconductors

Y. Adachi, T. Goto, K. Watanabe

Research output: Contribution to journal › Article › peer-review

4 Citations (Scopus)

Abstract

The precursor filament of Gd123 superconductors was prepared by solution spinning through a homogeneous aqueous solution of the metallic acetates. The precursor sample was partially melted in flowing 1% O₂ + Ar under various heating conditions. The maximum J_c value of 2.1 × 10⁴ A/cm² at 77 K and zero field was attained for filamentary Gd_1.18Ba_2.12Cu_3.09O_y superconductors. The sample had well aligned texture. The field dependence of J_c for the sample was investigated. An angle dependence of J_c along the filament diameter was detected. The J_c value above 1 × 10³ A/cm² was obtained at 77 K and 10 T.

Original language	English
Pages (from-to)	1077-1080
Number of pages	4
Journal	Physica C: Superconductivity and its Applications
Volume	357-360
Issue number	SUPPL. 1
DOIs	https://doi.org/10.1016/S0921-4534(01)00551-2
Publication status	Published - 2001 Sep
Externally published	Yes

Keywords

Field dependence of J
Filamentary Gd-Ba-Cu-O
Oxygen controlled melt growth

ASJC Scopus subject areas

Condensed Matter Physics

Access to Document

10.1016/S0921-4534(01)00551-2

Cite this

@article{9bd09df3ce61440ba2af9960572c2b5c,

title = "Oxygen controlled melt growth process of filamentary Gd123 superconductors",

abstract = "The precursor filament of Gd123 superconductors was prepared by solution spinning through a homogeneous aqueous solution of the metallic acetates. The precursor sample was partially melted in flowing 1% O2 + Ar under various heating conditions. The maximum Jc value of 2.1 × 104 A/cm2 at 77 K and zero field was attained for filamentary Gd1.18Ba2.12Cu3.09Oy superconductors. The sample had well aligned texture. The field dependence of Jc for the sample was investigated. An angle dependence of Jc along the filament diameter was detected. The Jc value above 1 × 103 A/cm2 was obtained at 77 K and 10 T.",

keywords = "Field dependence of J, Filamentary Gd-Ba-Cu-O, Oxygen controlled melt growth",

author = "Y. Adachi and T. Goto and K. Watanabe",

year = "2001",

month = sep,

doi = "10.1016/S0921-4534(01)00551-2",

language = "English",

volume = "357-360",

pages = "1077--1080",

journal = "Physica C: Superconductivity and its Applications",

issn = "0921-4534",

publisher = "Elsevier",

number = "SUPPL. 1",

}

TY - JOUR

T1 - Oxygen controlled melt growth process of filamentary Gd123 superconductors

AU - Adachi, Y.

AU - Goto, T.

AU - Watanabe, K.

PY - 2001/9

Y1 - 2001/9

N2 - The precursor filament of Gd123 superconductors was prepared by solution spinning through a homogeneous aqueous solution of the metallic acetates. The precursor sample was partially melted in flowing 1% O2 + Ar under various heating conditions. The maximum Jc value of 2.1 × 104 A/cm2 at 77 K and zero field was attained for filamentary Gd1.18Ba2.12Cu3.09Oy superconductors. The sample had well aligned texture. The field dependence of Jc for the sample was investigated. An angle dependence of Jc along the filament diameter was detected. The Jc value above 1 × 103 A/cm2 was obtained at 77 K and 10 T.

AB - The precursor filament of Gd123 superconductors was prepared by solution spinning through a homogeneous aqueous solution of the metallic acetates. The precursor sample was partially melted in flowing 1% O2 + Ar under various heating conditions. The maximum Jc value of 2.1 × 104 A/cm2 at 77 K and zero field was attained for filamentary Gd1.18Ba2.12Cu3.09Oy superconductors. The sample had well aligned texture. The field dependence of Jc for the sample was investigated. An angle dependence of Jc along the filament diameter was detected. The Jc value above 1 × 103 A/cm2 was obtained at 77 K and 10 T.

KW - Field dependence of J

KW - Filamentary Gd-Ba-Cu-O

KW - Oxygen controlled melt growth

UR - http://www.scopus.com/inward/record.url?scp=0035451217&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0035451217&partnerID=8YFLogxK

U2 - 10.1016/S0921-4534(01)00551-2

DO - 10.1016/S0921-4534(01)00551-2

M3 - Article

AN - SCOPUS:0035451217

VL - 357-360

SP - 1077

EP - 1080

JO - Physica C: Superconductivity and its Applications

JF - Physica C: Superconductivity and its Applications

SN - 0921-4534

IS - SUPPL. 1

ER -

Oxygen controlled melt growth process of filamentary Gd123 superconductors

Abstract

Keywords

ASJC Scopus subject areas

Access to Document

Other files and links

Fingerprint

Cite this