Oxidation of Silicon Nanopillars

Shujun Ye, Kikuo Yamabe, Tetsuo Endoh

Research output: Contribution to journalArticlepeer-review

1 Citation (Scopus)

Abstract

Systematic investigation of dry oxidation of sub-100 nm diameter Si nanopillars (NPs) of various diameters under varying conditions reveals that at 900 °C, the oxidation involves a deep self-limiting oxidation step where the oxidation nearly stops, and the consumed Si thickness (y) exhibits a first-order-reaction-like relation, y = a1 × (1 - exp (-b1 × t)), under an oxidation time t. At 1000 °C, the high oxidation rate with a slight self-limiting step is observed and small NPs could be entirely oxidized. In this case, the relation changes to y = a2 × t^b2. The above equations are confirmed to be applicable for all reported Si NPs and nanowires. Importantly, the relation y^2 ∝ t that is widely used for Si oxidation in traditional theories can only express oxidation of planar, concave, and large convex surfaces but not for Si NPs and nanowires. Since the oxide around Si NPs is found to grow radially and has a lower density compared to that on the planar surfaces oxidized under the same conditions, oxidation-induced stress in Si and/or tensile stress in oxides is considered to dominate the oxidation of Si NPs via affecting the reaction rate constant instead of oxidant diffusion inhibition. This study contributes to a deeper understanding of the oxidation of nanostructured Si, as well as nanostructured metals. It also supports the precise design/fabrication of Si NP-based sub-10 nm devices such as gate-all-around transistors, optoelectronic devices, and biosensors.

Original languageEnglish
Pages (from-to)8853-8861
Number of pages9
JournalJournal of Physical Chemistry C
Volume125
Issue number16
DOIs
Publication statusPublished - 2021 Apr 29

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Energy(all)
  • Physical and Theoretical Chemistry
  • Surfaces, Coatings and Films

Fingerprint

Dive into the research topics of 'Oxidation of Silicon Nanopillars'. Together they form a unique fingerprint.

Cite this