Abstract
The order-disorder and martensitic transitions of Ni-Al-Mn Heusler alloys aged at low temperatures were investigated. The aging at 400 °C induced the ordering from B2 to the L21 structure and that the endothermic peak of the heating curve at 500 °C was due to disordering from the L21 to the B2 structure.
| Original language | English |
|---|---|
| Pages (from-to) | 2225-2227 |
| Number of pages | 3 |
| Journal | Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science |
| Volume | 29 A |
| Issue number | 8 |
| DOIs | |
| Publication status | Published - 1998 Jan 1 |
ASJC Scopus subject areas
- Condensed Matter Physics
- Mechanics of Materials
- Metals and Alloys
Fingerprint Dive into the research topics of 'Ordering and martensitic transformations of Ni<sub>2</sub>AlMn Heusler alloys'. Together they form a unique fingerprint.
Cite this
Sutou, Y., Ohnuma, I., Kainuma, R., & Ishida, K. (1998). Ordering and martensitic transformations of Ni2AlMn Heusler alloys. Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, 29 A(8), 2225-2227. https://doi.org/10.1007/s11661-998-0047-8