Order-disorder transformation in Fe50Co50 particles synthesized by polyol process

G. B. Chon, K. Shinoda, S. Suzuki, B. Jeyadevan

Research output: Contribution to journalArticle

13 Citations (Scopus)

Abstract

X-ray diffraction applied anomalous dispersion effect was used for characterizing the order-disorder transformation in Fe50Co 50 fine particles synthesized by polyol process. The long range order parameter was estimated from the superlattice peak intensities in the diffraction pattern of particles annealed in the temperature range between 20 and 800°C. The results showed that fine particles of as-synthesized Fe-Co have a disordered structure at room temperature, while the ordered structure is present, to a great extent, in Fe-Co bulk alloys. The fine particles of the disordered alloy were transformed to the ordered state by annealing up to about 450°C. The magnetic properties of the Fe-Co alloy fine particles annealed at different temperatures were also investigated using a vibrating sample magnetometer, in which magnetic fields of up to 15 kOe were applied to samples at room temperature. The saturation magnetization of the as-synthesized particles increased with annealing temperature. This may be attributed to transformation from disordered to ordered structure, along with sintering.

Original languageEnglish
Pages (from-to)707-711
Number of pages5
JournalMaterials Transactions
Volume51
Issue number4
DOIs
Publication statusPublished - 2010 Apr 1

Keywords

  • Iron-cobalt particle
  • Order-disorder transformation
  • Structure
  • X-ray diffraction

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Order-disorder transformation in Fe<sub>50</sub>Co<sub>50</sub> particles synthesized by polyol process'. Together they form a unique fingerprint.

  • Cite this