Optimization of residual stress measurement conditions for a 2d method using x-ray diffraction and its application for stainless steel treated by laser cavitation peening

Hitoshi Soyama, Chieko Kuji, Tsunemoto Kuriyagawa, Christopher R. Chighizola, Michael R. Hill

Research output: Contribution to journalArticlepeer-review

Abstract

As the fatigue strength of metallic components may be affected by residual stress variation at small length scales, an evaluation method for studying residual stress at sub-mm scale is needed. The sin2ψ method using X-ray diffraction (XRD) is a common method to measure residual stress. However, this method has a lower limit on length scale. In the present study, a method using at a 2D XRD detector with ω-oscillation is proposed, and the measured residual stress obtained by the 2D method is compared to results obtained from the sin2ψ method and the slitting method. The results show that the 2D method can evaluate residual stress in areas with a diameter of 0.2 mm or less in a stainless steel with average grain size of 7 µm. The 2D method was further applied to assess residual stress in the stainless steel after treatment by laser cavitation peening (LCP). The diameter of the laser spot used for LCP was about 0.5 mm, and the stainless steel was treated with evenly spaced laser spots at 4 pulses/mm2. The 2D method revealed fluctuations of LCP-induced residual stress at sub-mm scale that are consistent with fluctuations in the height of the peened surface.

Original languageEnglish
Article number2772
JournalMaterials
Volume14
Issue number11
DOIs
Publication statusPublished - 2021 Jun 1

Keywords

  • Laser cavitation peening
  • Pulse laser
  • Residual stress
  • X-ray diffraction

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics

Fingerprint

Dive into the research topics of 'Optimization of residual stress measurement conditions for a 2d method using x-ray diffraction and its application for stainless steel treated by laser cavitation peening'. Together they form a unique fingerprint.

Cite this