Nitridation behavior of sapphire using a carbon-saturated N2 -CO gas mixture

Hiroyuki Fukuyama, Katsuhito Nakamura, Toshiaki Aikawa, Hidekazu Kobatake, Akira Hakomori, Kazuya Takada, Kenji Hiraga

Research output: Contribution to journalArticle

32 Citations (Scopus)

Abstract

The authors previously developed a sapphire nitridation method using carbon-saturated N2 -CO gas mixture to form a high-quality AlN film for III-nitride-based optoelectronic devices. In this study, the nitridation behavior of (0001) (c) plane and (11̄20) (a) plane sapphire was studied to elucidate and optimize the process at temperatures of 1823 and 1873 K. The AlN film thickness, surface morphology, crystal quality, and interfacial phenomena were investigated as functions of nitridation time and temperature. Fundamentally, the AlN film grows as a result of the diffusion process that occurs in the AlN film. The voids found at the AlN/sapphire interface indicate that the Al2O3 dissociates into Al3+ and O 2- ions, and that the ions diffuse in the AlN film. However, the growth rate of AlN film does not obey the simple diffusion model. The AlN film thickness has a maximum and decreases slightly with time, which indicates that the thermal decomposition of AlN film must be considered when comprehensively describing the nitridation process.

Original languageEnglish
Article number043502
JournalJournal of Applied Physics
Volume107
Issue number4
DOIs
Publication statusPublished - 2010 Mar 15

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Nitridation behavior of sapphire using a carbon-saturated N<sub>2</sub> -CO gas mixture'. Together they form a unique fingerprint.

Cite this