Microstructures and interface magnetic moments in mn2val/fe layered films showing exchange bias

Takahide Kubota, Yusuke Shimada, Tomoki Tsuchiya, Tomoki Yoshikawa, Keita Ito, Yukiharu Takeda, Yuji Saitoh, Toyohiko J. Konno, Akio Kimura, Koki Takanashi

Research output: Contribution to journalArticlepeer-review

Abstract

Heusler alloys are a material class exhibiting various magnetic properties, including antiferromagnetism. A typical application of antiferromagnets is exchange bias that is a shift of the magnetization curve observed in a layered structure consisting of antiferromagnetic and ferromagnetic films. In this study, a layered sample consisting of a Heusler alloy, Mn2VAl and a ferromagnet, Fe, is selected as a material system exhibiting exchange bias. Although the fully ordered Mn2VAl is known as a ferrimagnet, with an optimum fabrication condition for the Mn2VAl layer, the Mn2VAl/Fe layered structure exhibits exchange bias. The appearance of the antiferromagnetic property in the Mn2VAl is remarkable; however, the details have been unclear. To clarify the microscopic aspects on the crystal structures and magnetic moments around the Mn2VAl/Fe interface, cross-sectional scanning transmission electron microscope (STEM) observation, and synchrotron soft X-ray magnetic circular dichroism (XMCD) measurements were employed. The high-angle annular dark-field STEM images demonstrated clusters of Mn2VAl with the L21 phase distributed only around the interface to the Fe layer in the sample showing the exchange bias. Furthermore, antiferromagnetic coupling between the Mn-and Fe-moments were observed in element-specific hysteresis loops measured using the XMCD. The locally ordered L21 phase and antiferromagnetic Mn-moments in the Mn2VAl were suggested as important factors for the exchange bias.

Original languageEnglish
Article number1723
JournalNanomaterials
Volume11
Issue number7
DOIs
Publication statusPublished - 2021 Jul

Keywords

  • Antiferromagnet
  • Exchange bias
  • Heusler alloy
  • TEM
  • XMCD

ASJC Scopus subject areas

  • Chemical Engineering(all)
  • Materials Science(all)

Fingerprint

Dive into the research topics of 'Microstructures and interface magnetic moments in mn<sub>2</sub>val/fe layered films showing exchange bias'. Together they form a unique fingerprint.

Cite this