Microstructures and hardness properties of laser clad Ni base two-phase intermetallic alloy coating

Takeshi Okuno, Yasuyuki Kaneno, Takuto Yamaguchi, Satoshi Semboshi, Hideki Hagino, Takayuki Takasugi

Research output: Contribution to journalArticlepeer-review

4 Citations (Scopus)

Abstract

The two-phase Ni3Al and Ni3V intermetallic alloy laser clad on substrate of SUS304 was evaluated by hardness measurement, scanning electron microscopy, electron probe microanalyzer and transmission electron microscopy observations, focusing on the effect of post annealing after laser irradiation. The laser clad coating layer was diluted with approximately 5.4 at.% Fe and 1.6 at.% Cr stemming from the substrate. In the as-clad coating layer, the inhomogeneous eutectoid microstructure due to incomplete phase separation into two intermetallic phases Ni3Al and Ni3V took place. The hardness in the as-clad coating layer was lower than that in post annealed coating layers. In the coating layer annealed at 1553 K for 5 h, a dual two-phase microstructure composed of the primary cuboidal Ni3Al surrounded by the channel regions in which the major constituent is the Ni3V phase was observed, indicating that the complete eutectoid microstructure was developed. In the coating layer annealed at 1248 K for 24 h, the developed microstructure was lamellar-like one composed of the Ni3Al and Ni3V phases. The hardness in the coating layer annealed at 1248 K was the highest in the coatings observed in this study.

Original languageEnglish
Pages (from-to)4531-4540
Number of pages10
JournalJournal of Materials Research
Volume32
Issue number24
DOIs
Publication statusPublished - 2017 Dec 28

Keywords

  • Coating
  • Laser
  • Microstructure

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Microstructures and hardness properties of laser clad Ni base two-phase intermetallic alloy coating'. Together they form a unique fingerprint.

Cite this