Microstructure in a plasma-nitrided Fe-18 mass% Cr alloy

G. Miyamoto, A. Yonemoto, Y. Tanaka, T. Furuhara, T. Maki

Research output: Contribution to journalArticle

41 Citations (Scopus)

Abstract

Microstructures in a nitrided zone of an Fe-18 mass% Cr binary alloy plasma-nitrided at temperatures between 743 and 943 K were investigated by means of electron microscopy. The morphology of the nitrided zone changed drastically depending on the nitriding temperatures. On nitriding at 943 K, disk- and rod-shaped CrN and rod-shaped Cr2N were observed in the original ferrite grains. Examination of orientation relationships between the ferrite matrix and the rod-shaped Cr nitrides suggested that a transition from Cr2N to CrN occurs during nitriding at 943 K. On nitriding at 843 K, elongated columnar-shaped ferrite grains containing regularly spaced lamellar CrN precipitates developed from the specimen surface and grew inwards. Most of the columnar ferrite grains held Σ9 coincidence site lattice relationships with respect to the original ferrite grains. The columnar ferrite tends to form at a lower nitriding temperature or a higher Cr content.

Original languageEnglish
Pages (from-to)4771-4779
Number of pages9
JournalActa Materialia
Volume54
Issue number18
DOIs
Publication statusPublished - 2006 Oct 1

Keywords

  • EBSD
  • Plasma nitriding
  • Precipitation
  • Steel
  • TEM

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Polymers and Plastics
  • Metals and Alloys

Fingerprint Dive into the research topics of 'Microstructure in a plasma-nitrided Fe-18 mass% Cr alloy'. Together they form a unique fingerprint.

  • Cite this