Microstructural changes in Nd2Fe14B permanent magnet alloys during HDDR phenomena

Research output: Contribution to journalArticlepeer-review

11 Citations (Scopus)

Abstract

Microstructural changes in Nd-Fe-B alloys during the hydrogénation, disproportionation, desorption, and recombination (HDDR) phenomena were studied by XRD and TEM. These phenomena are caused by a heat treatment in hydrogen (H-treatment), in which the disproportionation occurs, and a subsequent heat treatment in vacuum (V-treatment), in which the recombination reaction occurs. The disproportionated mixture is formed of submicron sized colonies, which consist of NdH2 rods embedded in an a-Fe matrix, at the first stage of the disproportionation reaction. Some relationship in crystallographic orientation was observed among the NdH2, α-Fe, and the undecomposed Nd2Fe14B phases. H-treatment at higher temperatures causes the grain growth of the disproportionated phases, but the relationship in crystallographic orientation remains between the NdH 2 and α-Fe phases. The recombined Nd2Fe14B grains in the alloys V-treated at temperatures higher than 800°C, exhibit the same texture as the original, untreated alloys, and this grain alignment appears to begin as the recombination reaction occurs. The alloys V-treated at temperatures lower than 800°C show isotropic characteristics.

Original languageEnglish
Pages (from-to)482-488
Number of pages7
JournalMaterials Transactions, JIM
Volume37
Issue number3
DOIs
Publication statusPublished - 1996

Keywords

  • Anisotropic magnets
  • Disproportionation reaction
  • HDDR
  • Ndzfeub
  • Recombination reaction

ASJC Scopus subject areas

  • Engineering(all)

Fingerprint Dive into the research topics of 'Microstructural changes in Nd<sub>2</sub>Fe<sub>14</sub>B permanent magnet alloys during HDDR phenomena'. Together they form a unique fingerprint.

Cite this