Mechanical properties of titanium/aluminum composite material by Compression Shearing Method at Room Temperature

M. Horita; N. Nakayama; N. Saito; H. Miki; H. Takeishi; H. Mugishima; T. Suzuki

Mechanical properties of titanium/aluminum composite material by Compression Shearing Method at Room Temperature

M. Horita, N. Nakayama, N. Saito, H. Miki, H. Takeishi, H. Mugishima, T. Suzuki

Advanced Interdisciplinary Research Division

Research output: Chapter in Book/Report/Conference proceeding › Conference contribution

1 Citation (Scopus)

Abstract

In this study, to produce Ti/Al thin plate, Ti/Al mixed powders were formed by Compression Shearing Method at Room Temperature (COSME-RT). COSME-RT is adding a compressive stress and shear strain at the same time on the metal powders in air, and a thin plate metal can be obtained. Then, the Ti content ratio was changing from 25 to 75 vol.%. Their mechanical properties were measured. As a result, tensile strength of 75vol.%Ti was around 400 MPa, the value was similar to rolled Ti (ASTM grade 2).

Original language	English
Title of host publication	ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials
Publisher	European Conference on Composite Materials, ECCM
ISBN (Print)	9788888785332
Publication status	Published - 2012
Event	15th European Conference on Composite Materials: Composites at Venice, ECCM 2012 - Venice, Italy Duration: 2012 Jun 24 → 2012 Jun 28

Publication series

Name	ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials

Other

Other	15th European Conference on Composite Materials: Composites at Venice, ECCM 2012
Country/Territory	Italy
City	Venice
Period	12/6/24 → 12/6/28

Keywords

Aluminum
Composite metal
Sever plastic deformation
Titanium

ASJC Scopus subject areas

Ceramics and Composites

Cite this

Horita, M., Nakayama, N., Saito, N., Miki, H., Takeishi, H., Mugishima, H., & Suzuki, T. (2012). Mechanical properties of titanium/aluminum composite material by Compression Shearing Method at Room Temperature. In ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials (ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials). European Conference on Composite Materials, ECCM.

Mechanical properties of titanium/aluminum composite material by Compression Shearing Method at Room Temperature. / Horita, M.; Nakayama, N.; Saito, N.; Miki, H.; Takeishi, H.; Mugishima, H.; Suzuki, T.

ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials. European Conference on Composite Materials, ECCM, 2012. (ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials).

Research output: Chapter in Book/Report/Conference proceeding › Conference contribution

Horita, M, Nakayama, N, Saito, N, Miki, H, Takeishi, H, Mugishima, H & Suzuki, T 2012, Mechanical properties of titanium/aluminum composite material by Compression Shearing Method at Room Temperature. in ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials. ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials, European Conference on Composite Materials, ECCM, 15th European Conference on Composite Materials: Composites at Venice, ECCM 2012, Venice, Italy, 12/6/24.

Horita M, Nakayama N, Saito N, Miki H, Takeishi H, Mugishima H et al. Mechanical properties of titanium/aluminum composite material by Compression Shearing Method at Room Temperature. In ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials. European Conference on Composite Materials, ECCM. 2012. (ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials).

Horita, M. ; Nakayama, N. ; Saito, N. ; Miki, H. ; Takeishi, H. ; Mugishima, H. ; Suzuki, T. / Mechanical properties of titanium/aluminum composite material by Compression Shearing Method at Room Temperature. ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials. European Conference on Composite Materials, ECCM, 2012. (ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials).

@inproceedings{1c301fac53fc471c902fa3e77ccf476c,

title = "Mechanical properties of titanium/aluminum composite material by Compression Shearing Method at Room Temperature",

abstract = "In this study, to produce Ti/Al thin plate, Ti/Al mixed powders were formed by Compression Shearing Method at Room Temperature (COSME-RT). COSME-RT is adding a compressive stress and shear strain at the same time on the metal powders in air, and a thin plate metal can be obtained. Then, the Ti content ratio was changing from 25 to 75 vol.%. Their mechanical properties were measured. As a result, tensile strength of 75vol.%Ti was around 400 MPa, the value was similar to rolled Ti (ASTM grade 2).",

keywords = "Aluminum, Composite metal, Sever plastic deformation, Titanium",

author = "M. Horita and N. Nakayama and N. Saito and H. Miki and H. Takeishi and H. Mugishima and T. Suzuki",

year = "2012",

language = "English",

isbn = "9788888785332",

series = "ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials",

publisher = "European Conference on Composite Materials, ECCM",

booktitle = "ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials",

note = "15th European Conference on Composite Materials: Composites at Venice, ECCM 2012 ; Conference date: 24-06-2012 Through 28-06-2012",

}

TY - GEN

T1 - Mechanical properties of titanium/aluminum composite material by Compression Shearing Method at Room Temperature

AU - Horita, M.

AU - Nakayama, N.

AU - Saito, N.

AU - Miki, H.

AU - Takeishi, H.

AU - Mugishima, H.

AU - Suzuki, T.

PY - 2012

Y1 - 2012

N2 - In this study, to produce Ti/Al thin plate, Ti/Al mixed powders were formed by Compression Shearing Method at Room Temperature (COSME-RT). COSME-RT is adding a compressive stress and shear strain at the same time on the metal powders in air, and a thin plate metal can be obtained. Then, the Ti content ratio was changing from 25 to 75 vol.%. Their mechanical properties were measured. As a result, tensile strength of 75vol.%Ti was around 400 MPa, the value was similar to rolled Ti (ASTM grade 2).

AB - In this study, to produce Ti/Al thin plate, Ti/Al mixed powders were formed by Compression Shearing Method at Room Temperature (COSME-RT). COSME-RT is adding a compressive stress and shear strain at the same time on the metal powders in air, and a thin plate metal can be obtained. Then, the Ti content ratio was changing from 25 to 75 vol.%. Their mechanical properties were measured. As a result, tensile strength of 75vol.%Ti was around 400 MPa, the value was similar to rolled Ti (ASTM grade 2).

KW - Aluminum

KW - Composite metal

KW - Sever plastic deformation

KW - Titanium

UR - http://www.scopus.com/inward/record.url?scp=84903954555&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84903954555&partnerID=8YFLogxK

M3 - Conference contribution

AN - SCOPUS:84903954555

SN - 9788888785332

T3 - ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials

BT - ECCM 2012 - Composites at Venice, Proceedings of the 15th European Conference on Composite Materials

PB - European Conference on Composite Materials, ECCM

T2 - 15th European Conference on Composite Materials: Composites at Venice, ECCM 2012

Y2 - 24 June 2012 through 28 June 2012

ER -

Mechanical properties of titanium/aluminum composite material by Compression Shearing Method at Room Temperature

Abstract

Publication series

Other

Keywords

ASJC Scopus subject areas

Other files and links

Fingerprint

Cite this