TY - JOUR
T1 - Long-range ordered structure of Ti-B-C-N in a TiB2- TiC x N1-x eutectic composite
AU - Cheng, Eric Jianfeng
AU - Katsui, Hirokazu
AU - Tu, Rong
AU - Goto, Takashi
N1 - Copyright:
Copyright 2014 Elsevier B.V., All rights reserved.
PY - 2014/8
Y1 - 2014/8
N2 - A TiB2-TiCxN1-x quasi-binary eutectic composite, with a rod-like faceted texture and a long-range ordered structure of Ti-B-C-N, was prepared by the arc-melting of TiB2, TiC, and TiN powders. Hexagonal single-crystalline TiCxN1-x rods were grown in a single-crystalline TiB2 matrix with a crystal orientation relationship of TiB2 (112̄0)//TiCxN1-x (2̄02) and TiB2 [0001]//TiCxN1-x [111]. A long-range ordered structure of Ti-B-C-N was formed by the intermixing of the coherent interplanar spacings of seven TiB2 (0001) and nine TiC xN1-x (111) planes.
AB - A TiB2-TiCxN1-x quasi-binary eutectic composite, with a rod-like faceted texture and a long-range ordered structure of Ti-B-C-N, was prepared by the arc-melting of TiB2, TiC, and TiN powders. Hexagonal single-crystalline TiCxN1-x rods were grown in a single-crystalline TiB2 matrix with a crystal orientation relationship of TiB2 (112̄0)//TiCxN1-x (2̄02) and TiB2 [0001]//TiCxN1-x [111]. A long-range ordered structure of Ti-B-C-N was formed by the intermixing of the coherent interplanar spacings of seven TiB2 (0001) and nine TiC xN1-x (111) planes.
UR - http://www.scopus.com/inward/record.url?scp=84905591116&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=84905591116&partnerID=8YFLogxK
U2 - 10.1111/jace.13118
DO - 10.1111/jace.13118
M3 - Article
AN - SCOPUS:84905591116
SN - 0002-7820
VL - 97
SP - 2423
EP - 2426
JO - Journal of the American Ceramic Society
JF - Journal of the American Ceramic Society
IS - 8
ER -