Lattice strain in bulk GaN epilayers grown on CrN/sapphire template

S. W. Lee, Jun Seok Ha, Hyun Jae Lee, Hyo Jong Lee, H. Goto, T. Hanada, T. Goto, Katsushi Fujii, M. W. Cho, T. Yao

Research output: Contribution to journalArticlepeer-review

49 Citations (Scopus)

Abstract

Microphotoluminescence spectroscopy is used to investigate local strain in GaN films grown on c -sapphire with CrN buffer, where the CrN buffer is partly etched. Biaxial compressive strain dominates GaN films grown on CrN buffer/ c -plane sapphire. The emission energies of D0 X, F XA, and F XA -1LO emission lines shift gradually from a high value to a low one, as the excitation laser beam scans from the unetched side of the sample to the etched side, while the emission intensities show only a slight change. No cracking occurs in the GaN film during etching except a change in bending of the detached part of the GaN film from convex to concave as determined by surface profiler. Both the lattice parameter and the energy position of the bound exciton emission peaks from a completely detached GaN are almost the same as those reported for strain-free GaN. The line width of the (0002) ω scan of a GaN film is narrowed from 352 to 331 arc sec through detaching presumably due to decrease in bending. Those properties suggest that gradual lattice strain relaxation takes place in GaN layers grown on CrN buffer as etching of CrN buffer proceeds and that the chemical lift-off enables to detach a GaN film from a sapphire substrate without generating defects.

Original languageEnglish
Article number082105
JournalApplied Physics Letters
Volume94
Issue number8
DOIs
Publication statusPublished - 2009

ASJC Scopus subject areas

  • Physics and Astronomy (miscellaneous)

Fingerprint

Dive into the research topics of 'Lattice strain in bulk GaN epilayers grown on CrN/sapphire template'. Together they form a unique fingerprint.

Cite this