Laser welding of 2198-T851 Al-Li alloy with filler wire

Kaili Lin, Wuxiong Yang, Ting Huang, Rongshi Xiao

Research output: Contribution to journalArticlepeer-review

Abstract

2198-T851 Aluminum-Lithium alloy is a new high-strength material with low density, high specific strength, good corrosion resistance and well properties in low temperature condition. 2198-T851 with a thickness of 1.8 mm is welded with 2319 filler wire (Al-Cu) by using 6 kW fiber laser on butt welding. The effect of welding parameters on the weld formation and hot cracking are investigated, as well as testing the mechanical properties of the joint and analyzing of fracture morphology. The results indicate that a good joint with well weld formation and no hot cracks is obtained under the appropriate laser power, welding speed and wire feeding rate. The average tensile strength of joint reaches to 272 MPa and the extension rate of joint is 1.6%, the tensile fracture happens in the weld zone with ductile fracture characteristics.

Original languageEnglish
Article numbers216001
JournalGuangxue Xuebao/Acta Optica Sinica
Volume35
DOIs
Publication statusPublished - 2015 Sep 10
Externally publishedYes

Keywords

  • Aluminum-Lithium alloy
  • Fiber laser
  • Hot cracking
  • Laser technique
  • Microstructure and property
  • Weld formation

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Atomic and Molecular Physics, and Optics

Fingerprint

Dive into the research topics of 'Laser welding of 2198-T851 Al-Li alloy with filler wire'. Together they form a unique fingerprint.

Cite this