Irradiation-induced shrinkage of highly crystalline SiC fibers

Sosuke Kondo, Tatsuya Hinoki, Makoto Nonaka, Kazumi Ozawa

Research output: Contribution to journalArticlepeer-review

26 Citations (Scopus)

Abstract

Composites consisting of a SiC matrix prepared by chemical vapor infiltration that was reinforced by Tyranno™ SA3rd (TSA3) or Hi-Nicalon™ Type S (HNLS) SiC fibers were irradiated with 5.1 MeV Si ions to 100 dpa at 300 °C. It was confirmed that the irradiated microstructure of TSA3 was stable up to 100 dpa. In contrast, the results of surface profilometry and cross-sectional transmission electron microscopy (TEM) showed that HNLS fibers underwent 0.8% shrinkage along the axis and 0.7% radial shrinkage. High-resolution TEM images of the highly damaged regions in the HNLS material revealed the complete loss of carbon ribbons initially distributed at the SiC grain boundaries. Ion-beam-induced diffusion of carbon into the SiC grains was indicated from the observations of the interdiffusion layer formed at the fiber/pyrocarbon interface.

Original languageEnglish
Pages (from-to)1-9
Number of pages9
JournalActa Materialia
Volume83
DOIs
Publication statusPublished - 2015 Jan 15
Externally publishedYes

Keywords

  • Irradiation effect
  • Microstructure
  • SiC fibers
  • SiC/SiC composites

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Polymers and Plastics
  • Metals and Alloys

Fingerprint

Dive into the research topics of 'Irradiation-induced shrinkage of highly crystalline SiC fibers'. Together they form a unique fingerprint.

Cite this