Interactive effect of impurities on giant magnetoresistance of Co-Fe/Cu multilayers

Masakiyo Tsunoda, Hideo Arai, Daisuke Takahashi, Satoshi Miura, Migaku Takahashi

Research output: Contribution to journalArticlepeer-review

8 Citations (Scopus)

Abstract

Giant magnetoresistance of Co-Fe-B/Cu multilayers fabricated in the sputtering atmosphere, where the amount of oxygen impurity is varied, is discussed in connection with their interfacial roughness. The magnetoresistance (MR) ratio of Co-Fe/Cu multilayers is enhanced by up to 33% when the oxygen content is varied between 10 and 100 ppm of processing Ar gas. The enhancement of the MR ratio was due to the flattening effect of impurity oxygen on the multilayer interfaces: the root mean square roughness of the multilayer was decreased from 7.5 to 5Å. With increasing boron content in Co-Fe layers, however, the enhancing effect of MR ratio by oxygen diminished and nearly vanished for 12at%-B-(Co-Fe) case. The strong affinity of boron for oxygen is suggested as a probable mechanism.

Original languageEnglish
Pages (from-to)189-191
Number of pages3
JournalJournal of Magnetism and Magnetic Materials
Volume240
Issue number1-3
DOIs
Publication statusPublished - 2002 Feb 1

Keywords

  • Giant magnetoresistance
  • Impurities
  • Interface roughness
  • Multilayer
  • Thin films

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics

Fingerprint Dive into the research topics of 'Interactive effect of impurities on giant magnetoresistance of Co-Fe/Cu multilayers'. Together they form a unique fingerprint.

Cite this