Influence of grain size and veneer firing process on the flexural strength of zirconia ceramics

Keisuke Nakamura, Erik Adolfsson, Percy Milleding, Taro Kanno, Ulf Örtengren

Research output: Contribution to journalArticle

22 Citations (Scopus)

Abstract

The aim of the present investigation was to study the influence of grain size on the strength of yttria-stabilized zirconia upon exposure to an additional heat treatment, mimicking the veneering process. The green bodies of zirconia discs prepared by cold isostatic pressing were sintered at 1,425, 1,500, or 1,575°C to customize the grain size. The disc-shaped specimens were highly polished and then processed with or without additional heat treatments (five times at 850-930°C). Ten specimens from each treatment group were subjected to a biaxial flexural strength test according to the ISO 6872 standard. The grain size of the specimens was analyzed by the mean linear intercept technique using scanning electron microscopy. It was demonstrated that the mechanical strength of zirconia ceramics was not reduced by the veneer firing processes when polished specimens were used, but the strength was found to decrease with increasing grain size. The raw materials and the sintering process used should be selected appropriately to avoid grain coarsening because it was found that the strength was influenced by large grains.

Original languageEnglish
Pages (from-to)249-254
Number of pages6
JournalEuropean Journal of Oral Sciences
Volume120
Issue number3
DOIs
Publication statusPublished - 2012 Jun

Keywords

  • Flexural strength
  • Grain size
  • Heat treatment
  • Sintering
  • Zirconia

ASJC Scopus subject areas

  • Dentistry(all)

Fingerprint Dive into the research topics of 'Influence of grain size and veneer firing process on the flexural strength of zirconia ceramics'. Together they form a unique fingerprint.

  • Cite this