In-doped multifilled n-type skutterudites with ZT = 1.8

G. Rogl, A. Grytsiv, K. Yubuta, S. Puchegger, E. Bauer, C. Raju, R. C. Mallik, P. Rogl

Research output: Contribution to journalArticle

77 Citations (Scopus)

Abstract

In this paper we maximize the thermoelectric (TE) figure of merit, ZT, of n-type skutterudites, (In, Sr, Ba, Yb)yCo4Sb12, via three different routes: (i) find the optimum fraction of In as fourth filler (ii) check the influence of powder particle, grain, and crystallite size on the TE properties and (iii) check thermal stability. Filled n-type (Sr, Ba, Yb)yCo4Sb12 was mixed in three different proportions with In0.4Co4Sb12, ball milled (regular or high-energy (HB) ball milling) and hot-pressed. Particle size analyses and SEM pictures of the broken surfaces of the hot pressed samples document that only HB produces uniform particles/grains with average crystallite sizes ∼100 nm, proven by transmission electron microscopy. X-ray Rietveld refinements combined with EDX indicate that in all cases indium entered the icosahedral voids of the skutterudite. Temperature dependent physical properties of all three regularly ball-milled samples show that increasing In-content infers an increasing electrical resistivity, increasing Seebeck coefficient but a decreasing total thermal conductivity. Although ZT (823 K) is in the same range as for the sample without In, the ZT values in the whole temperature range are higher and consequently the TE-conversion efficiency, η is at least 10% higher. Annealing the samples at 600 °C for three days shows minor changes in structure and thermoelectric properties, indicating TE stability. The HB sample, due to uniformly small particles, equally sized grains and crystallites, exhibits a high power factor (4.4 mW/m K-2 at 730 K) and a very low thermal conductivity leading to an outstanding high ZT = 1.8 at 823 K (ηmax = 17.5%).

Original languageEnglish
Pages (from-to)201-211
Number of pages11
JournalActa Materialia
Volume95
DOIs
Publication statusPublished - 2015 Jun 16

Keywords

  • Nanostructured materials
  • Transmission electron microscopy (TEM)
  • Transport properties

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Polymers and Plastics
  • Metals and Alloys

Fingerprint Dive into the research topics of 'In-doped multifilled n-type skutterudites with ZT = 1.8'. Together they form a unique fingerprint.

  • Cite this

    Rogl, G., Grytsiv, A., Yubuta, K., Puchegger, S., Bauer, E., Raju, C., Mallik, R. C., & Rogl, P. (2015). In-doped multifilled n-type skutterudites with ZT = 1.8. Acta Materialia, 95, 201-211. https://doi.org/10.1016/j.actamat.2015.05.024