Chemistry
Irradiation-Assisted Stress Corrosion Cracking
100%
Stress Corrosion Cracking
10%
Atom
10%
Impurity
10%
Annealing
5%
Aqueous Solution
5%
Sensitization
5%
Phase Composition
5%
Cracking (Chemical)
5%
Environment
5%
Degradation
5%
Segregation
5%
Bolt
5%
Engineering
Pressurized Water Reactor
30%
Grain Boundary
15%
Chromium Content
15%
Stress Corrosion Cracking
10%
Stainless Steel
10%
Primary Water
10%
Elements
10%
Steel
10%
Tensile Test
5%
Chemical Composition
5%
Light Water Reactors
5%
Annealing
5%
Silicon Content
5%
Bulk Composition
5%
Cracking Susceptibility
5%
Internal Component
5%
Radiation
5%
Environment
5%
Internals
5%
Bolts
5%
Physics
Fracture Toughness
30%
Strain Rate
15%
Impurities
10%
Stress Corrosion Cracking
10%
Chromium
10%
Steel
10%
Cores
10%
Annealing
5%
Chemical Composition
5%
Degradation
5%
Matrix
5%
Cracking (Fracture)
5%
Environment
5%
Estimates
5%
Nickel
5%
Plant
5%
Material Science
Austenitic Stainless Steel
75%
Material
20%
Impurity
10%
Spring Steel
10%
Stainless Steel
10%
Solution
5%