Hydrogen in nanostructured vanadium-hydrogen systems

S. Orimo, Frank Kimmerle Günter Majer

Research output: Contribution to journalArticlepeer-review

40 Citations (Scopus)

Abstract

Nanostructured vanadium-hydrides, β2 - VHx, with typical grain sizes of 80 nm (x=0.82), 30 nm (x = 0.73), and 10 nm (x = 0.67) were prepared by mechanical milling under hydrogen atmosphere. The final grain size, about 10 nm, does not change any more with increasing milling time, and a homogeneous amorphous phase is not formed in this system, even after milling for 300 min. The hydrogen concentration in the grains xG decreases with decreasing grain size from xG = 0.82 in 80-nm grains to 0.72 in 10-nm grains. This indicates a modification of the β2 - γ phase boundary in the V-H system with nanometer-scale grains. The hydrogen concentration in the intergrains, xIG ≈ 0.5-0.6, is smaller than in the grains, and was found to be nearly independent of the grain size. The hydrogen diffusivity has been studied by NMR measurements of the proton spin-lattice relaxation Γ1. Generally, the measured Γ1 consists of contributions that result from both hydrogen in the grains and in the intergrain regions. Due to the smaller spin-spin relaxation rate Γ2 of the protons in the intergrain regions, their contribution to Γ1 could be measured separately by the spin-echo technique. The relaxation data indicate that, at a given temperature, the hydrogen diffusivity in the intergrain regions is substantially higher than inside the grains. The frequency dependence of the dipolar contribution Γ1,dip reveals a distribution in the activation enthalpy for hydrogen in the intergrain regions. This distribution was found to be the broader the smaller the grain size. A change in the diffusion mechanisms, presumably arising from the β2 - δ phase transition, takes place at about 200 K. The exchange of hydrogen atoms between the grains and the intergrain regions occurs very slowly and is negligible on the time scale given by Γ1.

Original languageEnglish
Article number094307
Pages (from-to)943071-9430710
Number of pages8487640
JournalPhysical Review B - Condensed Matter and Materials Physics
Volume63
Issue number9
DOIs
Publication statusPublished - 2001
Externally publishedYes

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics

Fingerprint Dive into the research topics of 'Hydrogen in nanostructured vanadium-hydrogen systems'. Together they form a unique fingerprint.

Cite this