Hydrogen absorption of Nb-Al alloy bulk specimens

Hideki Hosoda, Tatsuo Tabaru, Satoshi Semboshi, Shuji Hanada

Research output: Contribution to journalArticle

11 Citations (Scopus)

Abstract

Pulverization by hydrogenation is applicable to powder fabrication for refractory intermetallic alloys. Hydrogen absorption of various Nb-Al alloys containing 0-28 mol% Al was investigated using bulk specimens in a Sieverts-type apparatus at test temperatures of 313-373 K under hydrogen pressure of 0-3.4 MPa. The lattice parameter of Nb solid solution (Nbss) was determined precisely as a function of Al concentration. It was found that (1) the lattice parameter of Nbss is linearly reduced with increasing Al content, and (2) hydrogen absorption of Nbss is also remarkably reduced by Al addition. The atomic radius of Al in Nbss is determined to be 139.2 pm. Large hydrogen absorption more than 0.5 mass% H is observed only for pure Nb and Nb3Al-based two-phase alloys. However, pulverization and the large hydrogen absorption at a constant pressure (plateau) take place only in the latter alloys. This plateau does not stand for equilibrium hydride formation, but for rapid absorption through increased surface area by pulverization. These aspects are discussed in connection with hydrogen diffusivity.

Original languageEnglish
Pages (from-to)268-274
Number of pages7
JournalJournal of Alloys and Compounds
Volume281
Issue number2
DOIs
Publication statusPublished - 1998 Dec 18

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Hydrogen absorption of Nb-Al alloy bulk specimens'. Together they form a unique fingerprint.

  • Cite this