High-pressure synthesis of novel hydride in Mg-Ni (-H) system

Riki Kataoka, Yasuyuki Goto, Atsunori Kamegawa, Hitoshi Takamura, Masuo Okada

Research output: Contribution to journalArticlepeer-review

13 Citations (Scopus)

Abstract

A novel hydride was synthesized in Mg-Ni-H system by high pressure technique using a cubic-anvil-type apparatus. Crystal structure, thermal stability and hydrogen content of the hydride were studied. The novel hydride with a composition of MgNi2Hy was synthesized at 973 K for 2 h under the pressure of more than 2GPa, and was found to exhibit the body-centered tetragonal structure (space group 14/mmm, No. 139) with lattice parameters of a = 0.327(3) nm, c = 0.878(9) nm. Moreover, this hydride could be synthesized from each starting material, such as MgNi2 high pressure phase, MgNi2 (C36) and mixture of MgH2-x mol% Ni (x = 65-70). Its hydrogen content was estimated to be 2.23 mass% from fusion analysis and corresponding chemical formula was found to be MgNi2H 3.2. This hydride was decomposed into MgNi2 (C36) over 460 K. and has solubility of Ni content and thermal stability of the novel hydride was decreased with increasing Ni content.

Original languageEnglish
Pages (from-to)1957-1960
Number of pages4
JournalMaterials Transactions
Volume47
Issue number8
DOIs
Publication statusPublished - 2006 Aug

Keywords

  • High pressure
  • Hydride
  • Magnesium

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'High-pressure synthesis of novel hydride in Mg-Ni (-H) system'. Together they form a unique fingerprint.

Cite this