Hardness and wear properties of Ti-Mo-C-N film

Toshiaki Toyoda, Yuji Suto, Shoko Komiyama, Daisuke Ando, Junichi Koike, Mei Wang

Research output: Contribution to journalArticle

Abstract

The hardness and wear properties of Ti-Mo-C-N films were investigated by nanoindentation and ball-on-disc measurements, respectively. Ti-Mo-C-N films were deposited onto a stainless steel substrate by a reactive RF magnetron sputtering in the mixture of argon (7.5 ccm) and nitrogen (0-6.0 ccm) gases using Ti25Mo25C50 target. Ti-Mo-C film deposited without nitrogen gas flow showed a hardness of 34.8 GPa. The hardness drastically decreased with increasing nitrogen gas flow rate (/n2) and reached to a minimum hardness of 16.4 GPa at fN2=2.0 ccm. Contrarily, at overf N2=3;0 ccm, the hardness drastically increased with increasingf N2 and reached a maximal value of 32 GPa, and then slightly decreased again with further increase of fn2. It was found by TEM observation that the drastic decrease in hardness is caused by the formation of nanocrystalline microstructure, while the increase in hardness is due to the microstructural change from nanocrystalline to columner structure. The friction coefficient decreased with increasing fn2 and the film deposited at fN2=5.0 ccm showed a minimum value of 0.27. The simple oxidation test in air indicated that lubricious M0O3 is easy to be formed in the film deposited at a high/N2, which should cause the reduction of friction coefficient.

Original languageEnglish
Pages (from-to)220-226
Number of pages7
JournalNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
Volume79
Issue number4
DOIs
Publication statusPublished - 2015 Apr 1

Keywords

  • Friction coefficient
  • Hardness
  • Titanium-molybdenum-carbonitride
  • Wear resistance

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Hardness and wear properties of Ti-Mo-C-N film'. Together they form a unique fingerprint.

  • Cite this