Growth of epitaxial orthorhombic YO1.5-substituted HfO2 thin film

Takao Shimizu, Kiliha Katayama, Takanori Kiguchi, Akihiro Akama, Toyohiko J. Konno, Hiroshi Funakubo

Research output: Contribution to journalArticle

70 Citations (Scopus)

Abstract

YO1.5-substituted HfO2 thin films with various substitution amounts were grown on (100) YSZ substrates by the pulsed laser deposition method directly from the vapor phase. The epitaxial growth of film with different YO1.5 amounts was confirmed by the X-ray diffraction method. Wide-area reciprocal lattice mapping measurements were performed to clarify the crystal symmetry of films. The formed phases changed from low-symmetry monoclinic baddeleyite to high-symmetry tetragonal/cubic fluorite phases through an orthorhombic phase as the YO1.5 amount increased from 0 to 0.15. The additional annular bright-field scanning transmission electron microscopy indicates that the orthorhombic phase has polar structure. This means that the direct growth by vapor is of polar orthorhombic HfO2-based film. Moreover, high-temperature X-ray diffraction measurements showed that the film with a YO1.5 amount of 0.07 with orthorhombic structure at room temperature only exhibited a structural phase transition to tetragonal phase above 450°C. This temperature is much higher than the reported maximum temperature of 200°C to obtain ferroelectricity as well as the expected temperature for real device application. The growth of epitaxial orthorhombic HfO2-based film helps clarify the nature of ferroelectricity in HfO2-based films (186 words/200 words).

Original languageEnglish
Article number032910
JournalApplied Physics Letters
Volume107
Issue number3
DOIs
Publication statusPublished - 2015 Jul 20

ASJC Scopus subject areas

  • Physics and Astronomy (miscellaneous)

Fingerprint Dive into the research topics of 'Growth of epitaxial orthorhombic YO<sub>1.5</sub>-substituted HfO<sub>2</sub> thin film'. Together they form a unique fingerprint.

  • Cite this