Grain-boundary sliding in AZ31 magnesium alloys at room temperature to 523 K

J. Koike, R. Ohyama, T. Kobayashi, M. Suzuki, K. Maruyama

Research output: Contribution to journalArticlepeer-review

250 Citations (Scopus)

Abstract

Rolled sheets of AZ31 Mg alloys were subjected to tensile testing at temperatures ranging from room temperature to 523 K. The occurrence of grain-boundary sliding (GBS) at room temperature was demonstrated by the displacement of scribed lines across grain boundaries of deformed samples. Surface relief of deformed samples was measured by use of a scanning laser microscope. GBS strain was calculated from the measured surface step height, and its temperature dependence was analyzed by a Dorn-type constitutive equation. GBS above 423 K was found to be pure GBS that was activated by resolved applied shear stress acting on grain boundaries. The activation energy for GBS was found to be 80 kJ/mol, which is in agreement with the activation energy for grain boundary diffusion. Meanwhile, GBS below 373 K was found to be slip-induced GBS, and its extent was found to be significantly greater than that expected from extrapolation of high-temperature values. The slip-induced GBS is considered to occur by plastic compatibility conditions in the presence of plastic strain anisotropy and by absorption and dissociation of lattice dislocations at grain boundaries.

Original languageEnglish
Pages (from-to)445-451
Number of pages7
JournalMaterials Transactions
Volume44
Issue number4
DOIs
Publication statusPublished - 2003 Apr

Keywords

  • Grain-boundary sliding
  • Magnesium
  • Mechanical property
  • Room temperature

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Grain-boundary sliding in AZ31 magnesium alloys at room temperature to 523 K'. Together they form a unique fingerprint.

Cite this