Ge dots formation using Si(100)-c(4×4) surface reconstruction

Yuhki Satoh, Yuhki Itoh, Tomoyuki Kawashima, Katsuyoshi Washio

Research output: Contribution to journalArticle

5 Citations (Scopus)

Abstract

An effect of Si(100)-c(4×4) surface reconstruction by using sub-monolayer carbon reaction was investigated to form Ge dots on a Si (100) substrate. Samples were prepared by a solid-source molecular beam epitaxy system with an electron beam gun for carbon (C) sublimation and a Knudsen cell for Ge evaporation. C of 0.1 to 0.5 ML was deposited on Si (100) at the substrate temperature of 200 C, followed by a high-temperature treatment at 1000 C to react C with Si. Ge equivalent to 3 nm thick was subsequently deposited at 450 C. The densest dots were obtained for C coverage of 0.25 ML because the Si surface was stabilized by C for c(4×4) reconstruction without leaving excessive C. To investigate effects of Ge deposition thickness and temperature on Ge dot morphology, Ge equivalent to 3 to 5 nm thick was deposited at 400 and 450 C in the case of 0.25-ML C. The most uniform and densest Ge dots were formed at the Ge deposition thickness and temperature of 4 nm and 400 C, respectively. These results indicate that the Ge deposition should be optimized along the condition of the surface reconstruction via the C-Si reaction.

Original languageEnglish
Pages (from-to)1-4
Number of pages4
JournalJournal of Crystal Growth
Volume438
DOIs
Publication statusPublished - 2016 Mar 15

Keywords

  • A1. Low dimensional structures
  • A1. Nanostructures
  • A3. Molecular beam epitaxy
  • B2. Semiconducting germanium

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Inorganic Chemistry
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Ge dots formation using Si(100)-c(4×4) surface reconstruction'. Together they form a unique fingerprint.

  • Cite this