Fracture characteristics and microstructures of intermetallic compound Ti-24Al-11Nb (at%)

Mitsuo Niinomi, Toshiro Kobayashi, Masahiko Iwai, Tomoaki Hirota, J. C. Williams, A. W. Thompson

Research output: Contribution to journalArticlepeer-review

2 Citations (Scopus)

Abstract

Fracture characteristics of Ti-24Al-11Nb(at%) were related to microstructures based on the results of tensile tests and fracture toughness tests. Fracture mechanisms were also investigated. Fracture toughness, JIc, increased when microcracks were formed at the interfaces of colonies or acicular α2 in β solutionized and furnace cooled materials. The microcracks were formed by the coarse and big slip bands which were activated widely near the crack tip as a result of the formation of colonies. The crack propagation resistance, Tmat, increased with increasing crack deflection and shear ligaments in addition to microcracks. JIc and Tmat decreased with increasing precipitations of fine α2 in β during air cooling in α2 + β solutionized and air cooled materials. The blunting of the crack tip was inhibited because the deformability of β was inhibited by the finely precipitated α2. The microstructure of equiaxed α2 which is obtained by the solutionizing at 1313 K for 7.2 ks followed by water quenching gave the best balance among strength, elongation and fracture toughness.

Original languageEnglish
Pages (from-to)708-716
Number of pages9
JournalNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
Volume59
Issue number7
DOIs
Publication statusPublished - 1995

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Fracture characteristics and microstructures of intermetallic compound Ti-24Al-11Nb (at%)'. Together they form a unique fingerprint.

Cite this