Formation of icosahedral quasicrystalline phase in Zr70TM10Pd20 (TM = Fe, Co, or Cu) ternary glassy alloys

M. Matsushita, J. Saida, C. Li, A. Inoue

Research output: Contribution to journalArticlepeer-review

33 Citations (Scopus)


A nanoscale icosahedral quasicrystalline phase was confirmed as a primary precipitation phase in the melt-spun Zr70TM10Pd20 (TM = Fe, Co, or Cu) ternary glassy alloys with a two-stage crystallization process. The onset temperature of the transformation from amorphous to icosahedral phase is 713 K for Fe-, 696 K for Co-, and 680 K for Cu-containing alloys at the heating rate of 0.67 Ks-1. The size of the icosahedral particles is in the range of 20 to 50 nm for the Zr70Cu10Pd20 glassy alloy annealed for 120 s at 720 K. The icosahedral phase has a very fine particle size in a diameter range below 10 nm for the Zr70Fe10Pd20 and Zr70Co10Pd20 alloys. The crystallization reaction after the first exothermic peak results in the transition from the icosahedral to crystalline phases through a sharp exothermic reaction. Thus, the formation of the nanoscale icosahedral phase indicates the possibility that an icosahedral short-range order exists in the present glassy alloys.

Original languageEnglish
Pages (from-to)1280-1283
Number of pages4
JournalJournal of Materials Research
Issue number6
Publication statusPublished - 2000 Jun
Externally publishedYes

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering


Dive into the research topics of 'Formation of icosahedral quasicrystalline phase in Zr<sub>70</sub>TM<sub>10</sub>Pd<sub>20</sub> (TM = Fe, Co, or Cu) ternary glassy alloys'. Together they form a unique fingerprint.

Cite this