Formation of (111) orientation-controlled ferroelectric orthorhombic HfO2 thin films from solid phase via annealing

Takanori Mimura, Kiliha Katayama, Takao Shimizu, Hiroshi Uchida, Takanori Kiguchi, Akihiro Akama, Toyohiko J. Konno, Osami Sakata, Hiroshi Funakubo

Research output: Contribution to journalArticle

18 Citations (Scopus)

Abstract

0.07YO1.5-0.93HfO2 (YHO7) films were prepared on various substrates by pulse laser deposition at room temperature and subsequent heat treatment to enable a solid phase reaction. (111)-oriented 10 wt. % Sn-doped In2O3(ITO)//(111) yttria-stabilized zirconia, (111)Pt/TiOx/SiO2/(001)Si substrates, and (111)ITO/(111)Pt/TiOx/SiO2/(001)Si substrates were employed for film growth. In this study, X-ray diffraction measurements including θ-2θ measurements, reciprocal space mappings, and pole figure measurements were used to study the films. The film on (111)ITO//(111)yttria-stabilized zirconia was an (111)-orientated epitaxial film with ferroelectric orthorhombic phase; the film on (111)ITO/(111)Pt/TiOx/SiO2/(001)Si was an (111)-oriented uniaxial textured film with ferroelectric orthorhombic phase; and no preferred orientation was observed for the film on the (111)Pt/TiOx/SiO2/(001)Si substrate, which does not contain ITO. Polarization-hysteresis measurements confirmed that the films on ITO covered substrates had saturated ferroelectric hysteresis loops. A remanent polarization (Pr) of 9.6 and 10.8 μC/cm2 and coercive fields (Ec) of 1.9 and 2.0 MV/cm were obtained for the (111)-oriented epitaxial and uniaxial textured YHO7 films, respectively. These results demonstrate that the (111)-oriented ITO bottom electrodes play a key role in controlling the orientation and ferroelectricity of the phase formation of the solid films deposited at room temperature.

Original languageEnglish
Article number052903
JournalApplied Physics Letters
Volume109
Issue number5
DOIs
Publication statusPublished - 2016 Aug 1

ASJC Scopus subject areas

  • Physics and Astronomy (miscellaneous)

Fingerprint Dive into the research topics of 'Formation of (111) orientation-controlled ferroelectric orthorhombic HfO<sub>2</sub> thin films from solid phase via annealing'. Together they form a unique fingerprint.

  • Cite this