Fabrication and characterization of PDMS based magnetorheological elastomers

W. H. Li, M. Nakano

Research output: Contribution to journalArticle

58 Citations (Scopus)

Abstract

This paper presents the fabrication and characterization of a new magnetorheological elastomer (MRE) by using polydimethylsiloxane (PDMS) as a matrix. The base and curing agent of PDMS with a weight ratio of 10:1 were mixed first as the carrying matrix, and then carbonyl iron particles were added to the matrix and stirred sufficiently. The final mixture was placed in a vacuum chamber to eliminate bubbles for 30 min and was moulded later to form membranes of 1 mm thickness. A total of four PDMS based MRE samples, with different weight fractions of 60%, 70%, 80%, and 90%, were fabricated. Their mechanical properties under both steady-state and dynamic loading conditions were tested. The effects of particle composition, magnetic field, strain amplitude and frequency on the MRE effects were summarized. With the increase of iron particle composition, the magnetorheological effects of the samples increase steadily. It is also noted that the initial modulus of the MRE samples shows an increasing trend with the iron particle composition. Additionally, the microstructures of the PDMS based MREs were also observed by a low vacuum scanning electric microscope (LV-SEM).

Original languageEnglish
Article number055035
JournalSmart Materials and Structures
Volume22
Issue number5
DOIs
Publication statusPublished - 2013 May

ASJC Scopus subject areas

  • Signal Processing
  • Civil and Structural Engineering
  • Atomic and Molecular Physics, and Optics
  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Fabrication and characterization of PDMS based magnetorheological elastomers'. Together they form a unique fingerprint.

  • Cite this