T1 - Experimental determination of phase equilibria in the Co-Cr-Ni system
AU - Omori, T.
AU - Sato, J.
AU - Shinagawa, K.
AU - Ohnuma, I.
AU - Oikawa, K.
AU - Kainuma, R.
AU - Ishida, K.
N1 - Funding Information:
This work was supported by the New Energy and Industrial Technology Development Organization (NEDO). Support from a Grant-in-Aid for Scientific Research from JSPS and a Grant for Excellent Graduate Schools from MEXT is also acknowledged.
PY - 2014/4
Y1 - 2014/4
N2 - The phase equilibria between the γ (A1) and liquid phases and those between the γ, ε (A3), σ (D8b) and α (A2) phases at temperatures between 750 and 1300 °C in the Co-Cr-Ni system were determined by differential scanning calorimetry and electron probe microanalysis. It was found that the γ solidus and liquidus temperatures decrease with increasing Cr or Ni content and that the difference between them increases with increasing Cr content. The phase equilibria at 800, 900, 1000, 1100, 1200 and 1300 °C were determined using two-or three-phase alloys, and the phase boundaries due to the magnetically induced phase separation in the γ and ε phases were also observed at 850, 800 and 750 °C by the diffusion couple method.
AB - The phase equilibria between the γ (A1) and liquid phases and those between the γ, ε (A3), σ (D8b) and α (A2) phases at temperatures between 750 and 1300 °C in the Co-Cr-Ni system were determined by differential scanning calorimetry and electron probe microanalysis. It was found that the γ solidus and liquidus temperatures decrease with increasing Cr or Ni content and that the difference between them increases with increasing Cr content. The phase equilibria at 800, 900, 1000, 1100, 1200 and 1300 °C were determined using two-or three-phase alloys, and the phase boundaries due to the magnetically induced phase separation in the γ and ε phases were also observed at 850, 800 and 750 °C by the diffusion couple method.
KW - differential scanning calorimetry (DSC)
KW - experimental phase equilibria
KW - liquidus
KW - ternary phase diagram
UR - http://www.scopus.com/inward/record.url?scp=84897107690&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=84897107690&partnerID=8YFLogxK
U2 - 10.1007/s11669-014-0292-z
DO - 10.1007/s11669-014-0292-z
M3 - Article
AN - SCOPUS:84897107690
VL - 35
SP - 178
EP - 185
JO - Bulletin of Alloy Phase Diagrams
JF - Bulletin of Alloy Phase Diagrams
SN - 1547-7037
IS - 2
ER -