Evaluation of thin amorphous calcium phosphate coatings on titanium dental implants deposited using magnetron sputtering

Sou Yokota, Naruhiko Nishiwaki, Kyosuke Ueda, Takayuki Narushima, Hiroshi Kawamura, Tetsu Takahashi

Research output: Contribution to journalArticle

17 Citations (Scopus)

Abstract

OBJECTIVE:: Calcium phosphate is used for dental material because of its biocompatibility and osteoconductivity. Amorphous calcium phosphate (ACP) coatings deposited by magnetron sputtering can control their thickness and absorbability. This study aimed to evaluate and characterize ACP coatings deposited via magnetron sputtering. It was hypothesized that ACP coatings would enhance bone formation and be absorbed rapidly in vivo. METHODS:: ACP coatings that are 0.5 μm in thickness were deposited via magnetron sputtering on dental implants. Uncoated implants served as controls. The effect of the ACP coatings in vivo was investigated in New Zealand white rabbit. To evaluate the effect of the ACP coatings on the bone response of the implants, the removal torque, implant stability quotient, and histomorphometric analysis were performed on the implants at 1, 2, and 4 weeks after implantation. RESULTS:: Results of the x-ray diffraction analyses confirmed the deposition of ACP coatings. Images from the scanning electron microscopy revealed that the coatings were dense, uniform, and 0.5 μm in thickness and that they were absorbed completely. Mechanical stability and bone formation in the case of the ACP-coated implants were higher than those of control. CONCLUSION:: These results suggest that implants coated with thin ACP layers improve implant fixation and accelerate bone response.

Original languageEnglish
Pages (from-to)343-350
Number of pages8
JournalImplant Dentistry
Volume23
Issue number3
DOIs
Publication statusPublished - 2014 Jun

Keywords

  • Amorphous calcium phosphate
  • Animal experiments
  • Dental implant coating
  • RF magnetron sputtering

ASJC Scopus subject areas

  • Oral Surgery

Fingerprint Dive into the research topics of 'Evaluation of thin amorphous calcium phosphate coatings on titanium dental implants deposited using magnetron sputtering'. Together they form a unique fingerprint.

  • Cite this