Evaluation of the microstructural contribution to the coercivity of fine-grained Nd-Fe-B sintered magnets

Togo Fukada, Masashi Matsuura, Ryota Goto, Nobuki Tezuka, Satoshi Sugimoto, Yasuhiro Une, Masato Sagawa

Research output: Contribution to journalArticlepeer-review

17 Citations (Scopus)

Abstract

The relationship between coercivity and the microstructural parameters α and N eff for grain refined Nd-Fe-B sintered magnets was examined. The parameter α describes the effect of grain misalignment and a decrease in the magnetocrystalline anisotropy of the Nd 2Fe 14B grains on the coercivity. The parameter N eff describes the influence of the demagnetizing field on the coercivity. These parameters were evaluated for Nd-Fe-B sintered magnets with three different grain sizes and the same composition. N eff decreased with grain refinement, while α varied only slightly with grain size. This implies that the decrease in the demagnetizing field increased the coercivity through grain refinement. Grain shape and asperity were then evaluated by the aspect ratio, angle of the grain to the direction of magnetization, and reverse circularity. Although the aspect ratio and angle of the grains were not related to the changes in N eff, variation of the average reverse circularity corresponded to the changes in N eff with grain refinement. Therefore, improving the asperity should increase the coercivity through grain refinement.

Original languageEnglish
Pages (from-to)1967-1971
Number of pages5
JournalMaterials Transactions
Volume53
Issue number11
DOIs
Publication statusPublished - 2012

Keywords

  • Coercivity
  • Grain refinement
  • Microstructural parameters
  • Neodymium-iron-boron sintered magnet

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Evaluation of the microstructural contribution to the coercivity of fine-grained Nd-Fe-B sintered magnets'. Together they form a unique fingerprint.

Cite this