Evaluation of irradiation hardening of ion-irradiated V-4Cr-4Ti and V-4Cr-4Ti-0.15Y alloys by nanoindentation techniques

Takeshi Miyazawa, Takuya Nagasaka, Ryuta Kasada, Yoshimitsu Hishinuma, Takeo Muroga, Hideo Watanabe, Takuya Yamamoto, Shuhei Nogami, Masahiko Hatakeyama

Research output: Contribution to journalArticle

19 Citations (Scopus)

Abstract

Irradiation hardening behavior of V-4Cr-4Ti and V-4Cr-4Ti-0.15Y alloys after Cu-ion beam irradiation were investigated with a combination between nanoindentation techniques and finite element method (FEM) analysis. The ion-irradiation experiments were conducted at 473 K with 2.4 MeV Cu2+ ions up to 7.6 dpa. For the unirradiated materials, the increase in nanoindentation hardness with decreasing indentation depth, so-called indentation size effect (ISE), was clearly observed. After irradiation, irradiation hardening in the measured depth was identified. Hardening behavior of bulk-equivalent hardness for V-4Cr-4Ti-0.15Y alloy was similar to that for V-4Cr-4Ti alloy. Y addition has little effect on irradiation hardening at 473 K. Adding the concept of geometrically necessary dislocations (GNDs) to constitutive equation of V-4Cr-4Ti alloy, the ISE was simulated. A constant value of α = 0.5 was derived as an optimal value to simulate nanoindentation test for ion-irradiated V-4Cr-4Ti alloy. Adding the term of irradiation hardening Δσirrad. to constitutive equation with α = 0.5, FEM analyses for irradiated surface of V-4Cr-4Ti alloy were carried out. The analytic data of FEM analyses based on neutron-irradiation hardening equivalent to 3.0 dpa agreed with the experimental data to 0.76 dpa. The comparison indicates that irradiation hardening by heavy ion-irradiation is larger than that by neutron-irradiation at the same displacement damage level. Possible mechanisms for extra hardening by heavy ion-irradiation are the processes that the injected Cu ions could effectively produce irradiation defects such as interstitials compared with neutrons, and that higher damage rate of ion-irradiation enhanced nucleation of irradiation defects and hence increased the number density of the defects compared with neutron-irradiation.

Original languageEnglish
Pages (from-to)440-444
Number of pages5
JournalJournal of Nuclear Materials
Volume455
Issue number1-3
DOIs
Publication statusPublished - 2014 Dec

ASJC Scopus subject areas

  • Nuclear and High Energy Physics
  • Materials Science(all)
  • Nuclear Energy and Engineering

Fingerprint Dive into the research topics of 'Evaluation of irradiation hardening of ion-irradiated V-4Cr-4Ti and V-4Cr-4Ti-0.15Y alloys by nanoindentation techniques'. Together they form a unique fingerprint.

  • Cite this