Epitaxially grown Cu2Sb-type MnGaGe films with large perpendicular magnetic anisotropy

Mingling Sun, Takahide Kubota, Keita Ito, Shigeki Takahashi, Yoshiyuki Hirayama, Yoshiaki Sonobe, Koki Takanashi

Research output: Contribution to journalArticle

Abstract

A perpendicularly magnetized film is essentially important for spintronics applications, such as spin-transfer-torque type magnetoresistive random access memories, STT-MRAMs, and large perpendicular anisotropy energy, K u, with small saturation magnetization, M s, is required for reducing the critical current for the STT induced magnetization switching phenomenon. In this study, an equiatomic intermetallic compound, MnGaGe, was investigated in epitaxially grown film samples. Perpendicularly magnetized films with an M s value of about 260 emu/cm3 at 300 K were fabricated onto MgO (100) single crystal substrates. The maximum value of K u was 8.1 × 106 erg/cm3 at room temperature. Microstructure analysis using a scanning transmission electron microscope atomically revealed the Cu2Sb type crystal structure in the film sample. First principles calculations were also carried out to discuss the electronic structure. Using the analysis of the projected density of states for 3d-orbitals, the hybridization of the 3d-orbitals was suggested as a possible factor for promoting magnetocrystalline anisotropy. The MnGaGe film with the large K u and relatively small M s would be potentially used for spintronics applications.

Original languageEnglish
Article number062402
JournalApplied Physics Letters
Volume116
Issue number6
DOIs
Publication statusPublished - 2020 Feb 10

ASJC Scopus subject areas

  • Physics and Astronomy (miscellaneous)

Fingerprint Dive into the research topics of 'Epitaxially grown Cu<sub>2</sub>Sb-type MnGaGe films with large perpendicular magnetic anisotropy'. Together they form a unique fingerprint.

  • Cite this