Enhancement of Oxygen Reduction Reaction Activity of Pd Core-Pt Shell Structured Catalyst on a Potential Cycling Accelerated Durability Test

Naoya Aoki, Hideo Inoue, Takashi Okawa, Yuta Ikehata, Akira Shirai, Hideo Daimon, Takayuki Doi, Yuki Orikasa, Yoshiharu Uchimoto, Hiroshi Jinnai, Shin Inamoto, Yuji Otsuka, Minoru Inaba

Research output: Contribution to journalArticlepeer-review

7 Citations (Scopus)

Abstract

Carbon-supported Pd core-Pt shell structured catalyst (Pt/Pd/C) was synthesized by a modified Cu under potential deposition/Pt displacement method without any precise potential control. The specific activity for oxygen reduction reaction (ORR) of the Pt/Pd/C catalyst increased by 5-fold after an accelerated durability test (ADT; rectangular wave potential cycling of 0.6 V (3 s)–1.0 V (3 s) performed in Ar-saturated 0.1 M HClO4 at 80 °C for 10,000 cycles), which enhanced ORR mass activity of the catalyst by 1.4-fold although its electrochemical surface area significantly decreased. TEM observation showed that the morphology of the catalyst particles changed into a spherical shape and the mean diameter decreased after the ADT. TEM-EDX compositional analysis revealed that the Pd core preferentially dissolved out and that the Pt shell was rearranged and thickened with the ADT. CV measurement using Bi3+ probe implied that the Pt(111) facet was partially formed on the Pt shell after the ADT. Furthermore, EXAFS analysis showed that the Pt–Pt bond distance of the Pt shell was shortened after the ADT. It was considered that the drastic enhancement in the ORR-specific activity of the catalyst after the ADT arises from the decrease in number of lowly coordinated surface Pt atoms, partially formed Pt(111) facet on the catalyst surface, and properly induced compressive strain in the Pt shell via the rearrangement of the Pt shell assisted by the preferential dissolution of the Pd core during the ADT. [Figure not available: see fulltext.].

Original languageEnglish
Pages (from-to)125-138
Number of pages14
JournalElectrocatalysis
Volume9
Issue number2
DOIs
Publication statusPublished - 2018 Mar 1

Keywords

  • Accelerated durability test
  • ORR activity enhancement
  • Pd core dissolution
  • Pd core–Pt shell structured catalyst
  • Pt shell rearrangement

ASJC Scopus subject areas

  • Electrochemistry

Fingerprint Dive into the research topics of 'Enhancement of Oxygen Reduction Reaction Activity of Pd Core-Pt Shell Structured Catalyst on a Potential Cycling Accelerated Durability Test'. Together they form a unique fingerprint.

Cite this