Electrochemical performance of highly amorphous GeO:X powders synthesized in different alcohols for use in Na- and Li-ion batteries

T. Kajita, T. Itoh

Research output: Contribution to journalArticle

3 Citations (Scopus)

Abstract

We synthesized highly amorphous GeOx powders by a solution synthesis method, in which NaGe was oxidized by alcohol and placed in distilled water. Further, we investigated the effect of the alcohol used during the solution synthesis method on the electrochemical Na- and Li-ion insertion/extraction performances of the powder sample. We compared the oxidation process as performed using various alcohols. The amorphous GeOx powder sample synthesized by oxidation in 2-propanol (secondary alcohol) exhibited good electrochemical performance with respect to Na- and Li-ion insertion/extraction, while the amorphous GeOx powders synthesized using methanol, ethanol, and 1-propanol (primary alcohol) showed poor performances. These powders consisted of large particles, which was the reason for their poor electrochemical performance. In particular, their cycling performance in a Na-ion cell was significantly lowered by the large particle size. Hence, during the solution synthesis process, the use of a secondary alcohol is the key to synthesizing highly amorphous GeOx powders with small particle sizes. Finally, electrolyte decomposition was also found to be one of the main causes for the deterioration of the cycling performance in a Na-ion cell, because the change in the volume of the GeOx particles during charging/discharging was smaller in the Na-ion cell than in a Li-ion cell.

Original languageEnglish
Pages (from-to)102109-102115
Number of pages7
JournalRSC Advances
Volume6
Issue number104
DOIs
Publication statusPublished - 2016 Jan 1

ASJC Scopus subject areas

  • Chemistry(all)
  • Chemical Engineering(all)

Fingerprint Dive into the research topics of 'Electrochemical performance of highly amorphous GeO<sub>:X</sub> powders synthesized in different alcohols for use in Na- and Li-ion batteries'. Together they form a unique fingerprint.

Cite this