Elastic properties of heat resistant steels after long-term creep exposure

K. Sawada, T. Ohmura, T. Ohba, K. Tsuzaki, F. Abe, K. Kimura, I. Nonaka

Research output: Contribution to journalArticlepeer-review

Abstract

In order to clarify the effect of microstructural change during ageing and creep on elastic modulus, the elastic moduli of aged, crept and serviced (service-exposed) materials were investigated. In ferritic steels, the elastic modulus obtained by ultrasonic pulse does not change after long-term ageing and creep although the formation of creep voids slightly decreases the elastic modulus. In SUS304 and SUS316, the elastic modulus evaluated by ultrasonic pulse increases during ageing due to precipitation of M23C6 carbides, Laves phase and σ phase though the elastic modulus decreases during creep because of the formation of creep voids on grain boundaries. The increased elastic modulus of aged material with a large amount of σ phase was regarded as that of composite consists of matrix and σ phase. For STBA24, the elastic modulus obtained by a high temperature tensile test decreases after long-term service. The tensile test at a higher strain rate was proposed to avoid underestimation of elastic modulus of serviced materials at high temperatures.

Original languageEnglish
Pages (from-to)179-185
Number of pages7
JournalMaterials at High Temperatures
Volume25
Issue number3
DOIs
Publication statusPublished - 2008 Nov 21

Keywords

  • Ageing
  • Elastic modulus
  • Long-term creep
  • Microstructural change

ASJC Scopus subject areas

  • Ceramics and Composites
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint

Dive into the research topics of 'Elastic properties of heat resistant steels after long-term creep exposure'. Together they form a unique fingerprint.

Cite this