Abstract
Effects of B on the magnetic properties and high frequency characteristics of the Fe7Co3 based thin films were investigated through the microstructural analysis. It was found that B addition was very effective in increasing anisotropy field and resistivity and in decreasing coercivity without much loss of saturation magnetization. These enhancements were shown to be strongly related to grain size, grain morphology and preferred orientations. As a result, a Fe55Co28B17 film with small dispersion angle of ∼ 0.5° showed the ferromagnetic resonance frequency of 3.3 GHz and a linear effective permeability of ∼350 up to 2 GHz.
Original language | English |
---|---|
Pages (from-to) | 2706-2708 |
Number of pages | 3 |
Journal | IEEE Transactions on Magnetics |
Volume | 40 |
Issue number | 4 II |
DOIs | |
Publication status | Published - 2004 Jul |
Keywords
- Fe-Co-B thin film
- Ferromagnetic resonance
- High frequency
- Soft magnetic property
- Texture
ASJC Scopus subject areas
- Electronic, Optical and Magnetic Materials
- Electrical and Electronic Engineering