Effect of the thermomechanical properties of no-flow underfill materials on interconnect reliability

Satoru Katsurayama, Hironori Tohmyoh

Research output: Contribution to journalArticle

2 Citations (Scopus)

Abstract

The demands on flip chip packaging are increasing as the requirement for miniaturization and thinner silicon chips rises. In encapsulating flip chip packages it is important to not only maintain the mountability, but also to control the warpage of the package. In this paper, three types of underfill material with different thermomechanical properties are prepared. The requirements for achieving both longer interconnect life and the mountability with lower warpage are investigated. Underfill material with higher Young's modulus shows a longer interconnect life. From the results of failure analysis after thermal cycling, cracking at the edges of the bumps is observed. It is found from finite element analysis that underfill material with higher Young's modulus can effectively reduce the strain accumulating inside the bump. Underfill material with a low coefficient of thermal expansion reduces warpage after chip assembly. Therefore, optimization of both Young's modulus and the coefficient of thermal expansion of the underfill material are essential in order to achieve higher interconnect reliability while maintaining higher mountability.

Original languageEnglish
Article number6459561
Pages (from-to)370-376
Number of pages7
JournalIEEE Transactions on Components, Packaging and Manufacturing Technology
Volume3
Issue number3
DOIs
Publication statusPublished - 2013 Feb 15

Keywords

  • Coefficient of thermal expansion
  • interconnect reliability
  • no-flow process
  • underfill material
  • warpage
  • Young's modulus

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Industrial and Manufacturing Engineering
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Effect of the thermomechanical properties of no-flow underfill materials on interconnect reliability'. Together they form a unique fingerprint.

  • Cite this