Effect of Nb content on plastic deformation behavior and deformation textures of Ti-Nb-Zr-Ta-O alloy

Yoichi Nii, Hee Young Kim, Shuichi Miyazaki

Research output: Contribution to journalArticlepeer-review

4 Citations (Scopus)

Abstract

Recently developed β-Ti alloy Gum Metal is one of attractive materials for biomedical applications due to its excellent combination of low Young's modulus and high strength. Gum Metal also exhibits other unique properties such as non-linear elasticity, plastic deformation without work-hardening. These multifunctional properties in Gum Metal are quite intriguing characteristics not only for practical applications but also for fundamental studies. However the mechanism is not fully understood yet. In this research, in order to obtain new information for special plastic deformation behavior of Gum Metal, the deformation texture and microstructure of Ti-(19-29)Nb-2Zr-0.7Ta-1.2O alloys including typical composition of Gum Metal were investigated by XRD measurement and TEM observation. The major deformation texture of Ti-(21-29)Nb-2Zr-0.7Ta-1. 2O alloys was {001}〈110〉 type. However, the maximum orientation density I max in orientation distribution functions (ODFs) strongly depends on Nb content and the maximum value was obtained at Ti-23Nb-2Zr-0.7Ta-1. 2O, indicating that the strongest deformation texture was formed in Gum Metal composition. TEM observation implied that the strong deformation texture formation in Gum Metal is due to its unique deformation mechanism.

Original languageEnglish
Pages (from-to)970-974
Number of pages5
JournalNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
Volume72
Issue number12
DOIs
Publication statusPublished - 2008 Dec

Keywords

  • Biomaterial
  • Deformation texture
  • Plastic deformation
  • Titanium alloy

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Effect of Nb content on plastic deformation behavior and deformation textures of Ti-Nb-Zr-Ta-O alloy'. Together they form a unique fingerprint.

Cite this