Effect of Na2O Addition on Phosphorus Dissolution from Steelmaking Slag with High P2O5 Content

Chuan ming Du, Xu Gao, Shigeru Ueda, Shin ya Kitamura

Research output: Contribution to journalArticlepeer-review

20 Citations (Scopus)

Abstract

Slag with high P2O5 content generated during the use of high-P iron ores is an important potential source of phosphate. Because the P-rich 2CaO·SiO2–3CaO·P2O5 solid solution in the slag was preferentially dissolved compared with other phases in aqueous solutions, selective leaching of P from slag with high P2O5 content was applied to recover soluble P in this study. To improve dissolution of the P-rich solid solution, the effects of Na2O addition on slag dissolution were investigated under different leaching conditions. The results show that a new 2CaO·SiO2–2CaO·Na2O·P2O5 solid solution was formed in the slag after Na2O was added, resulting in a higher dissolution ratio of P. However, at pH 7, further increase in Na2O content did not promote P dissolution because of phosphate precipitation. At pH 5, a better P dissolution was obtained and its dissolution ratio increased with an increase in Na2O content, indicating that Na2O addition promoted the dissolution of the solid solution from slag. In the citric acid solution, more than 90% of the solid solution was dissolved and the dissolution of the matrix phase was suppressed dramatically by Na2O addition, leading to a low dissolution ratio of Fe. An excellent selective leaching of P from slag was achieved.

Original languageEnglish
Pages (from-to)671-682
Number of pages12
JournalJournal of Sustainable Metallurgy
Volume3
Issue number4
DOIs
Publication statusPublished - 2017 Dec 1

Keywords

  • Citric acid
  • NaO addition
  • Phosphorus recovery
  • Selective leaching
  • Steelmaking slag

ASJC Scopus subject areas

  • Environmental Science (miscellaneous)
  • Mechanics of Materials
  • Metals and Alloys

Fingerprint

Dive into the research topics of 'Effect of Na<sub>2</sub>O Addition on Phosphorus Dissolution from Steelmaking Slag with High P<sub>2</sub>O<sub>5</sub> Content'. Together they form a unique fingerprint.

Cite this