Effect of carbon content on v-bending in high-strength tripaided dual-phase steel sheets with polygonal ferrite matrix

Akihiko Nagasaka, Tomohiko Hojo, Masaya Fujita, Takumi Ohashi, Mako Miyasaka, Yuki Shibayama, Eiji Akiyama

Research output: Contribution to journalArticlepeer-review

Abstract

Effect of carbon content on V-bending in high-strength TRIP-aided dual-phase (TDP) steel sheets with polygonal ferrite matrix was investigated for automobile applications. V-bending test was performed on a hydraulic testing machine at a processing speed of 1 mm/min, using a rectangular specimen (50 mm in length, 5 mm in width, 1.2 mm in thickness). The main results are as follows. (1) The (0.1-0.4)C-1.5Si-1.5Mn, mass% TDP steel sheets were able to perform V-bending by straininduced martensitic transformation of TRIP effect. On the other hand, ferrite-martensite dual-phase (MDP0) steel sheet of 900 MPa grade was not able to perform 90-degree V-bending because of initiation of crack in tension region. (2) The 0.4C-1.5Si-1.5Mn, mass% TDP4 steel sheet of 1 100 MPa grade was able to enable the 90-degree V-bending that considered an amount of springback (=2?1), in which the 1 and the 2 are a bending angle on loading and a bending angle after unloading respectively, of more than 2-degree by controlling a displacement of punch bottom dead center.

Original languageEnglish
Pages (from-to)608-616
Number of pages9
JournalIsij International
Volume61
Issue number2
DOIs
Publication statusPublished - 2021 Feb 15

Keywords

  • EBSD
  • TRIP steel sheet
  • V-bending
  • bending load
  • chemical composition
  • polygonal ferrite matrix.
  • residual stress
  • springback

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Effect of carbon content on v-bending in high-strength tripaided dual-phase steel sheets with polygonal ferrite matrix'. Together they form a unique fingerprint.

Cite this