Effect of boron particle size on microstructure and superconducting properties of in-situ Cu addition MgB2 multifilamentary wire

Y. Hishinuma, A. Kikuchi, Y. Shimada, S. Hata, T. Takeuchi, S. Yamada, A. Sagara

Research output: Contribution to journalConference articlepeer-review

3 Citations (Scopus)

Abstract

In previous studies, the secondary (impurity and non-reactive) phase and voids were observed in MgB2 matrix after the heat treatment, and then these are the lowering factors of critical current density (Jc) property. In order to improve Jc property by microstructure control of MgB2 matrix, the fine elemental boron powder as the raw material was carried out using the high-speed vibrated milling with tungsten carbide (WC) jar. The average particle size of metal boron powder was decreased from 1.14 μm to 0.20 μm by the high-speed vibrated milling. The various fine particle boron powders as the function of milling time were also prepared, and in-situ Cu addition MgB2 multifilamentary wires using these fine boron powders were fabricated. Critical transition temperature (Tc) value of Cu addition MgB2 wire using fine boron powder obtained to about 37 K. No change of the Tc property by the different particle sized boron powders was confirmed. In this paper, the comparisons of microstructure and superconducting properties between the different boron particle sizes were investigated.

Original languageEnglish
Article number022009
JournalJournal of Physics: Conference Series
Volume507
Issue numberPART 2
DOIs
Publication statusPublished - 2014
Externally publishedYes
Event11th European Conference on Applied Superconductivity, EUCAS 2013 - Genoa, Italy
Duration: 2013 Sep 152013 Sep 19

ASJC Scopus subject areas

  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Effect of boron particle size on microstructure and superconducting properties of in-situ Cu addition MgB<sub>2</sub> multifilamentary wire'. Together they form a unique fingerprint.

Cite this