Effect of Al2O3 on high temperature mechanical properties of silicon nitride with Yb4Si2O7N2

Toshiyuki Nishimura, Mamoru Mitomo, Akira Ishida, Hidehiro Yoshida, Yuichi Ikuhara, Taketo Sakuma

    Research output: Contribution to journalArticle

    2 Citations (Scopus)

    Abstract

    Effect of Al2O3 on high temperature strength of silicon nitride with Yb4Si2O7N2 was investigated. A silicon nitride was fabricated by hot-pressing powder mixture including 87.4 mass% Si3N4, 12.1 mass% Yb2O3 and 0.5 mass% Al2O3. For reference, silicon nitride without Al2O3 addition was fabricated from powder mixture including 0.5 mass% SiO2 instead of Al2O3. Sinterability of silicon nitride with Al2O3 was higher than that of silicon nitride without Al2O3. Room temperature strength of the materials with Al2O3 was higher than that of the materials without Al2O3. Average strength at 1200 and 1350°C of both materials were almost same. The strength at 1500°C of the material with Al2O3 was slightly lower than that of the material without Al2O3. Creep resistance of the material with Al2O3 was lower than that of the materials without Al2O3.

    Original languageEnglish
    Pages (from-to)801-804
    Number of pages4
    JournalJournal of the Ceramic Society of Japan
    Volume105
    Issue number9
    DOIs
    Publication statusPublished - 1997 Sep

    Keywords

    • Alumina
    • Creep
    • High temperature strength
    • Silicon nitride
    • Ytterbium silicon oxynitride

    ASJC Scopus subject areas

    • Ceramics and Composites
    • Chemistry(all)
    • Condensed Matter Physics
    • Materials Chemistry

    Fingerprint Dive into the research topics of 'Effect of Al<sub>2</sub>O<sub>3</sub> on high temperature mechanical properties of silicon nitride with Yb<sub>4</sub>Si<sub>2</sub>O<sub>7</sub>N<sub>2</sub>'. Together they form a unique fingerprint.

  • Cite this