Dynamic fracture behavior of Ti-6Al-4V alloy with various stabilities of βphase

I. A. Akmoulin, M. Niinomi, T. Kobayashi

Research output: Contribution to journalArticle

17 Citations (Scopus)

Abstract

The effect of stability of the body-centered cubic (bcc) β phase on the dynamic fracture behavior of Ti-6Al-4V alloy at room temperature and 77 K has been studied. The presence of a highly unstable β phase in the quenched alloy leads to a decrease in both the dynamic fracture toughness and the crack propagation energy, and this decrease bccomes more pronounced when test temperature is reduced to 77 K. Somewhat improved fracture characteristics were obtained by applying anneal procedure to receive a fully stable β phase. The highest fracture toughness as well as the greatest crack propagation resistance were observed in the air-cooled grade, where the lattice parameter of the bcc phase was intermediate between those pertaining to quenched and annealed Ti-6Al-4V alloys. The effect is attributed to the vanadium content in the β phase, which is sufficiently high to suppress deformation-induced transformation. On the other hand, the V content should be low enough to retard ductile-brittle transition, typical for the bcc metals at cryogenic temperatures. As a result, marked toughening can be achieved, so that the lowest application temperature of high-strength titanium alloys containing the bcc phase can be decreased significantly.

Original languageEnglish
Pages (from-to)1655-1666
Number of pages12
JournalMetallurgical and Materials Transactions A
Volume25
Issue number8
DOIs
Publication statusPublished - 1994 Aug 1

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys

Fingerprint Dive into the research topics of 'Dynamic fracture behavior of Ti-6Al-4V alloy with various stabilities of βphase'. Together they form a unique fingerprint.

  • Cite this