Distribution of P2O5 between Solid Solution of 2CaO.Si02-3CaO.P2O5 and Liquid Phase

Farshid Pahlevani, Shin Ya Kitamura, Hiroyuki Shibata, Nobuhiro Maruoka

Research output: Contribution to journalArticlepeer-review

72 Citations (Scopus)

Abstract

It is desirable to decrease the phosphorous content of steel and the amount of slag in steel refining. For satisfying this requirement recently, the importance of multiphase slag in steel refining has been given considerable attention. Normally, hot metal dephosphorization slag consists of the CaO-Si02-FeO-P205 system, and the industrial operation is mainly carried out in the dicalcium silicate (C2S) saturated region. It is well known that C2S forms a solid solution with the main product of dephosphorization-tricalcium phosphate (C 3P)-at the treatment temperature over a wide composition range, and a high distribution ratio of P205 between the solid solution and the liquid phase has been reported. In order to determine the ruling factors on the distribution ratio, the influences of MgO, MnO, and A1203 were investigated for various slag compositions in the case of FeO or Fe203 as the iron oxide. First, a mixture of a standard regent was heated to the melting temperature in order to produce homogenous liquid slag. Next, it was cooled down to a semisolid state: during cooling, the solid solution of C3P-C2S was precipitated under the equilibrium condition. For clarifying the influence of slag composition on the distribution ratio, the ruling factors on the activity coefficient of P205 in the solid solution and liquid slag phase were evaluated. It is the contention of this research that the activity coefficient of P205 in the solid solution was largely influenced by P 205 and the total solved oxide content of the solid solution. (log γp2,O,5SS)cal was obtained empirically in order to represent the activity coefficient in the solid solution. On the other hand, the activity coefficient of P20 5 in the liquid phase was strongly influenced by the CaO content of the liquid phase. On the basic of these correlations, it was shown that the CaO content of the liquid phase and (log γp2,O,5SS) cal are the ruling factors on distribution ratio.

Original languageEnglish
Pages (from-to)822-829
Number of pages8
JournalIsij International
Volume50
Issue number6
DOIs
Publication statusPublished - 2010

Keywords

  • Activity coefficient of PO added oxide to slag
  • Distribution ratio
  • Multi phase slag
  • Steel refining

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Distribution of P<sub>2</sub>O<sub>5</sub> between Solid Solution of 2CaO.Si0<sub>2</sub>-3CaO.P<sub>2</sub>O<sub>5</sub> and Liquid Phase'. Together they form a unique fingerprint.

Cite this