Distribution of P2O5 between solid dicalcium silicate and liquid phases in CaO-SiO2-Fe2O3 system

Ken Ichi Shimauchi, Shin Ya Kitamura, Hiroyuki Shibata

Research output: Contribution to journalArticlepeer-review

72 Citations (Scopus)

Abstract

In most cases, the slag used in hot metal dephosphorization is saturated with dicalcium silicate (C2S) and contains two phases solid C 2S and liquid. It is known that C2S and tricalcium phosphate (C3P) form a solid solution over a wide range of composition. The distribution ratio of P2O5 between the solid solution and the liquid slag phase has been reported to be very high. In order to determine the maximum possible concentration of P2O 5 in the solid solution, the distribution ratio of P 2O5 in slag containing a high concentration of P 2O5 was measured in this study, and the influence of MgO and MnO on the distribution ratio was also investigated. CaO-SiO 2-Fe2O3 slag containing up to 18% P 2O5 was melted at 1 873 K and then cooled to 1 673 K at a rate of 10 K/min. During cooling, the solid solution of C2S and C3P precipitated from the liquid slag. A linear relationship, which was independent of the lime/silica ratio and P2O5 content, was found to exist between the distribution ratio of P2O5 and the T .Fe content. On the contrary, the concentration of P 2O5 in the solid solution was strongly influenced by the lime/silica ratio and P2O5 content. If the P 2O5 content was high enough and the T.Fe content was controlled to show the high distribution ratio, the concentration of C 3P in the solid solution can be increased to 100%. No significant change was observed in the distribution ratio upon the addition of MgO and MnO.

Original languageEnglish
Pages (from-to)505-511
Number of pages7
JournalIsij International
Volume49
Issue number4
DOIs
Publication statusPublished - 2009

Keywords

  • Dephosphorization
  • Hot metal pretreatment
  • Precipitation
  • Slag
  • Solid solution

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Distribution of P<sub>2</sub>O<sub>5</sub> between solid dicalcium silicate and liquid phases in CaO-SiO<sub>2</sub>-Fe<sub>2</sub>O<sub>3</sub> system'. Together they form a unique fingerprint.

Cite this