Direct observation of pit initiation process on type 304 stainless steel

Research output: Contribution to journalArticle

20 Citations (Scopus)

Abstract

In situ and real-time optical microscopic observations of pit initiation process on a commercial Type 304 stainless steel with low-sulfur content (0.004 mass%) were performed in 3M NaCl solution at 298 K. MnS inclusions with diameters of ca. 1 μm were found to act as the initiation sites of pitting, as was the case in a re-sulfurized Type 304 stainless steel (0.027 mass%). The pit was initiated at the boundary between the MnS inclusion and the steel matrix, and grew with time. After a few seconds, no visible change was observed for 1 s, even though the anodic current was measured, suggesting that the steel dissolution proceeded in the depth direction. After that, a small hole suddenly appeared on the steel surface. The hole widened with time, steadily becoming a large stable pit. This pit initiation process in the low-sulfur stainless steel is much like that found in the re-sulfurized stainless steel.

Original languageEnglish
Pages (from-to)857-860
Number of pages4
JournalMaterials Transactions
Volume55
Issue number5
DOIs
Publication statusPublished - 2014

Keywords

  • In situ observation
  • Initiation site of pitting
  • Manganese sulfide inclusion
  • Microelectrochemical technique
  • Pit
  • Type 304 stainless steel

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Direct observation of pit initiation process on type 304 stainless steel'. Together they form a unique fingerprint.

  • Cite this